摘要
A novel ionic cross-linked sulfonated poly(ether ether ketone) containing equal content of sulfonic acid and pendant tertiary amine groups (TA-SPEEK) has been initially synthesized for the application in direct methanol fuel cells (DMFC5). By adjusting the ratio of p-xylene dibromide to tertiary amine groups of TASPEEK, a series of ionic-covalent cross-linked membranes (C-SPEEK-x) with tunable degree of cross linking are prepared. Compared with the pristine membrane, the ionic and ionic-covalent cross-linked proton exchange membranes (PEMs) exhibit reduced methanol permeability and improved mechanical properties, dimensional and oxidative stability. The proton conductivity and methanol selectivity of protonated TA-SPEEK and C-SPEEK-x at 25 degrees C is up to 0.109 S cm(-1) and 3.88 x 105 S s cm(-3), respectively, which are higher than that of Nafion 115. The DMFC incorporating C-SPEEK-25 exhibits a maximum power density as high as 35.3 mW cm(-2) with 4 M MeOH at 25 degrees C (31.8 mW cm(-2) for Nafion 115). Due to the highly oxidative stability of the membrane, no obvious performance degradation of the DMFC is observed after more than 400 h operation, indicating such cost-effective ionic-covalent cross-linked membranes have substantial potential as alternative PEMs for DMFC applications. (C) 2017 Elsevier B.V. All rights reserved.